Laserfiche WebLink
E <br />Measurement <br />ASTM D5994 MIN: <br />(Modified) MAX: <br />Asperity GRI GM12: 30 mil AVE: <br />ODD #LOP EVEN #: BOTTOM <br />Specific Gravity <br />ASTM D792 <br />MFI ASTM D1238 <br />COND. E <br />GRADE: K307 <br />Carbon Black Content <br />ASTM D4218 <br />Carbon Black Dispersion <br />ASTM D5596 <br />11 JL. JL. nr_. JL. <br />aTuclimirg cce-w- rr iril ir u c cmiiro7�e <br />Lot #: <br />8180479 <br />Liner Type: MICROSPIKETM HDPE <br />METRIC <br />ENGLISH <br />Thickness......... <br />1.5 mm <br />60 mill <br />1.54 mm <br />61 mil <br />Length .............. <br />125 m <br />410.1 feet <br />N <br />441.4 <br />Width <br />7.00 m; <br />23.0 feet <br />1.63 mm <br />64 mil <br />............... <br />lbs <br />CERTIFIED <br />1.58 mm <br />62 mil <br />Hrs w/o Failures <br />TEST <br />@ 30% <br />OIT(Standard) ASTM D3895 <br />minutes 214 <br />RESULTS <br />�nsity <br />g/cc <br />.947 <br />Melt Flow Index 190°C /2160 g g/10 min <br />Range <br />Category <br />Tensile Strength <br />ASTM D6693 Average Strength @ Yield <br />ASTM D638 (Modified) <br />( 2 inches / minute ) <br />Average Strength @ Break <br />Elongation ASTM D6693 <br />ASTM D638 (Modified) Average Elongation @ Yield <br />( 2 inches /minute ) <br />Lo = 1.3" Yield <br />Lo = 2.0" Break Average Elongation @ Break <br />Dimensional Stability <br />ASTM D1204 (Modified) Average Dimensional change <br />Tear Resistance <br />ASTM D-1004 (Modified) Average 1 <br />----- - ....... ---- ------------- ___ <br />Puncture Resistance Load <br />FTMS 101 Method 2065 (Modified) <br />Puncture Resistance Load <br />ASTM D4833 (Modified) <br />— ---------- <br />ESCR Minimum <br />ASTM D1693 <br />Notched Constant Tensile Load pass /fail <br />ASTM D5397 <br />Customer: Allied Waste Industries <br />PO: BP0600139 Forward LF <br />Destination Manteca, CA <br />.24 <br />25 <br />N/mm 146 ppi <br />24 <br />N/mm 139 ppi <br />2,331 <br />psi <br />2,237 <br />psi <br />15.71 <br />279.7 <br />N <br />441.4 <br />ear Resistance <br />599.9 <br />N <br />1500 hrs <br />------------- -- <br />300 hrs <br />lbs <br />CERTIFIED <br />ONGOING <br />Hrs w/o Failures <br />@ 30% <br />.24 <br />25 <br />N/mm 146 ppi <br />24 <br />N/mm 139 ppi <br />2,331 <br />psi <br />2,237 <br />psi <br />15.71 <br />279.7 <br />N <br />441.4 <br />N <br />599.9 <br />N <br />1500 hrs <br />------------- -- <br />300 hrs <br />lbs <br />.24 <br />2.14 <br />10 in Cat I <br />2,331 <br />psi <br />2,237 <br />psi <br />15.71 <br />343.6 <br />—0.36 <br />62.887 <br />lbs <br />99.231 <br />lbs <br />134.86 <br />lbs <br />CERTIFIED <br />ONGOING <br />Date- 8-9-08 <br />Signa`tu're.'.��*4.X.'-47 <br />Quality Control Department 60HDmic.FRM <br />REV 03 <br />12/23/05 <br />