Specific GravityDensity g/cc \" <br />ASTM D792 .946 <br />MFI ASTM D1238 <br />COND. E Melt Flow Index 190°C /2160 g g/10 min .23 <br />GRADE: K307 <br />Carbon Black Content Range % 2.15 <br />ASTM D4218 <br />Carbon Black Dispersion Category 10 in Cat. 1 <br />ASTM D5596 <br />Tensile Strength \' <br />ASTM D6693 Average Strength @ Yield 34 N/mm 191 ppi 2,983 psi <br />ASTM D638 (Modified) <br />( 2 inches / minute ) <br />Average Strength @ Break 42 N/mm 238 ppi 3,706 psi <br />Elongation ASTM D6693 <br />N <br />ASTM D638 (Modified) <br />rr <br />, <br />N <br />11 <br />uCl <br />ilt u ��rifllll �1tyc�,tr� <br />ROLL # �930102-08Lot <br />#: <br />v�8280546 <br />_Liner Type:SS MICROSPIKETm HDPE <br />Measurement <br />METRIC <br />ENGLISH <br />Thickness......... 1.5 mm60 mil <br />ASTM D5994 MIN: <br />1.59 mm <br />63 mil <br />n <br />Length .............. 152.4 500.0 feet <br />(Modified) MAX: <br />1.70 mm <br />67 mil <br />Width ............... 7.00 m; 23.0 feet <br />Asperity GRI GM12: 33 mil AVE: <br />1.63 mm <br />64 mil <br />TEST <br />OIT(Standard) ASTM D3895 minutes 213 RESULTS <br />Specific GravityDensity g/cc \" <br />ASTM D792 .946 <br />MFI ASTM D1238 <br />COND. E Melt Flow Index 190°C /2160 g g/10 min .23 <br />GRADE: K307 <br />Carbon Black Content Range % 2.15 <br />ASTM D4218 <br />Carbon Black Dispersion Category 10 in Cat. 1 <br />ASTM D5596 <br />Tensile Strength \' <br />ASTM D6693 Average Strength @ Yield 34 N/mm 191 ppi 2,983 psi <br />ASTM D638 (Modified) <br />( 2 inches / minute ) <br />Average Strength @ Break 42 N/mm 238 ppi 3,706 psi <br />Elongation ASTM D6693 <br />N <br />ASTM D638 (Modified) <br />Average Elongation @ Yield <br />( 2 inches / minute ) <br />N <br />Lo = 1.3" Yield <br />lbs <br />Lo = 2.0" Break <br />Average Elongation @ Break <br />Dimensional Stability <br />lbs <br />ASTM D1204 (Modified) <br />Average Dimensional change <br />Tear Resistance <br />ASTM D-1004 (Modified) <br />Average Tear Resistance <br />Puncture Resistance <br />Load <br />FTMS 101 Method 2065 (Modified) <br />Puncture Resistance <br />Load <br />ASTM D4833 (Modified) <br />ESCR <br />Minimum Hrs w/o Failures <br />ASTM D1693 <br />Notched Constant Tensile Load <br />pass / fail @ 30% <br />ASTM D5397 <br />Customer: Allied Waste Industries <br />PO: BP0600139 Forward LF <br />Destination Manteca, CA <br />% 16.84 <br />% 562.6 <br />% ,-0.20 <br />315.8 <br />N <br />71.005 <br />lbs <br />501.9 <br />N <br />112.84 <br />lbs <br />635.5 <br />N <br />'142.86 <br />lbs <br />1500 hrs CERTIFIED <br />300 hrs pass <br />6-5-08 <br />Date* .........�W.AQ;�7 <br />Signature <br />Quality Control Department REV 02 MS.FRM <br />REV 02 <br />12/23/05 <br />