Laserfiche WebLink
T 1. <br />SEAM PEEL AND SHEAR TEST RESULTS <br />CLIENT.- VECTOR ENGINEERING MATERIAL: HDPE SEAM <br />PROJECT: Forward Landfill SEAM TYPE: Fusion Weld <br />DATE RECD: 18 -Aug -08 PGL JOB #: G081025 <br />11 <br />QC'd By: <br />TEST METHOD: ASTM D6392 <br />DATE REPORT.' 18 -Aug -08 <br />c.rossneaa speea: <br />z rnimm <br />ADHESION FAILURE. SPECIMENS DELAMINATED UNDER THE BEAD. <br />AD <br />Crosshead Speed: 2 in/min <br />AD2 <br />ADHESION FAILURE. <br />BRK <br />SH R EVAL ATIO <br />AD-WLD <br />PEEL EVALUATION <br />SE1 <br />SAMPLE <br />ID <br />DS -S1 <br />112 <br />PGL <br />CONTROL # <br />49803 <br />MAXIMUM <br />STRENGTH <br />14k width <br />205 <br />212 <br />% <br />Elongation <br />> 50% <br />> 50% <br />Locus <br />of <br />Break <br />BRK <br />BRK <br />PROJECT <br />SPEC. <br />Ibrn width <br />SPECIMEN <br />NUMBER <br />1 Outside <br />2 Outside <br />MAXIMUM <br />STRENGTH <br />Ibhn width <br />102 <br />116 <br />% <br />INCURSION <br />% <br />0 <br />0 <br />LOCUS <br />OF <br />BREAK <br />SE1 <br />SEI <br />PROJECT <br />SPEC. <br />Lb Lin width <br />SIP <br />SEPARATION IN THE PLANE OF THE SHEET. <br />211 <br />> 50% <br />BRK <br />3 Outside <br />120 <br />0 <br />SE1 <br />AD-BRK <br />BREAK IN FIRST SEAM AFTER SOME ADHESION FAILURE. <br />203 <br />> 50% <br />BRK <br />4 Outside <br />120 <br />0 <br />SE1 <br />210 <br />> 50% <br />BRK <br />5 Outside <br />1 110 <br />0 <br />SE1 <br />AVG: <br />114 <br />STD. DEV. <br />8 <br />1Inside <br />108 <br />0 <br />SE1 <br />2lnside <br />106 <br />0 <br />SE1 <br />3lnside <br />106 <br />0 <br />SE1 <br />4lnside <br />104 <br />0 <br />SE1 <br />5Inside <br />102 <br />0 <br />SE1 <br />AVG. <br />208 <br />AVG: <br />105 <br />STD. DEV. <br />4 <br />STD. DEV. <br />2 <br />DS -32 <br />49804 <br />203 <br />> 50% <br />BRK <br />1 Outside <br />118 <br />0 <br />SE1 <br />5/6 <br />209 <br />> 50% <br />BRK <br />2 Outside <br />116 <br />0 <br />SEI <br />213 <br />> 50% <br />BRK <br />3 Outside <br />114 <br />0 <br />SEI <br />215 <br />> 50% <br />BRK <br />4 Outside <br />112 <br />0 <br />SE1 <br />214 <br />> 50% <br />BRK <br />5 Outside <br />118 <br />0 <br />SE1 <br />AVG: <br />116 <br />STD. DEV. <br />3 <br />1Inside <br />110 <br />0 <br />SEI <br />2lnside <br />108 <br />0 <br />SE1 <br />3lnside <br />108 <br />0 <br />SE1 <br />4lnside <br />104 <br />0 <br />SE1 <br />5Inside <br />108 <br />0 <br />SEI <br />AVG: <br />211 <br />AVG: <br />108 <br />STD. DEV. <br />5 <br />STD. DEV. <br />2 <br />wacmat ucaunu-raan lamas uo,sac SION): EXTRUSION: <br />AD1 <br />ADHESION FAILURE. SPECIMENS DELAMINATED UNDER THE BEAD. <br />AD <br />ADHESION FAILURE. <br />AD2 <br />ADHESION FAILURE. <br />BRK <br />BREAK IN SHEETING. <br />AD-WLD <br />BREAK THROUGH THE FILLET. <br />SE1 <br />BREAK AT OUTER EDGE OF SEAM. <br />SE1 <br />BREAK AT BOTTOM EDGE OF SEAM. <br />SE2 <br />BREAK AT INNER EDGE OF SEAM. <br />SE2 <br />BREAK AT TOP EDGE OF SEAM. <br />AD-BRK <br />BREAK IN FIRST SEAM AFTER SOME ADHESION FAILURE, <br />SE3 <br />BREAK AT BOTTOM EDGE OF SEAM (for PEEL only) <br />SIP <br />SEPARATION IN THE PLANE OF THE SHEET. <br />BRK1 <br />BREAK IN BOTTOM SHEETING. <br />BRK2 <br />BREAK IN TOP SHEETING, <br />AD-BRK <br />BREAK IN FIRST SEAM AFTER SOME ADHESION FAILURE. <br />HT <br />BREAK AT EDGE OF HOT TACK <br />SIP SEPARATION IN THE PLANE OF THE SHEET. <br />Precision Geosynthetic Laboratories-�.b:- <br />