CLIENT: VECTOR ENGINEERING <br />PROJECT. • Forward Landfill <br />DATE RECD: 20 -Aug -08 <br />MATERIAL: HDPE SEAM <br />SEAM TYPE. Fusion Weld <br />PGL JOB #: G081049 <br />QC'd By: <br />TEST METHOD: ASTM D6392 <br />DATE REPORT. 20 -Aug -08 <br />Crosshead Speed: 2 inlmin Crosshead Speed. 2 in/min <br />SHEAR EVALUATION PEEL EVALUATION <br />MAXIMUM % Locus PROJECT MAXIMUM % LOCUS PROJECT <br />SAMPLE PGL STRENGTH Elongation of SPEC. SPECIMEN STRENGTH INCURSION OF SPEC. <br />ID CONTROL # Ib/n widthl Break /bfin width NUMBER Iblin width % BREAK Ib/in width <br />DS -S13 <br />49949 <br />199 <br />> 50% <br />BRK <br />1 Outside <br />142 <br />0 <br />SE1 <br />BREAK AT BOTTOM EDGE OF SEAM. <br />S37/36 <br />BREAK AT INNER EDGE OF SEAM. <br />200 <br />> 50% <br />BRK <br />2 Outside <br />130 <br />0 <br />SE1 <br />SEPARATION IN THE PLANE OF THE SHEET. <br />BRK1 <br />BREAK IN BOTTOM SHEETING. <br />206 <br />> 50% <br />BRK <br />3 Outside <br />138 <br />0 <br />SE1 <br />BREAK IN FIRST SEAM AFTER SOME ADHESION FAILURE. <br />208 <br />> 50% <br />BRK <br />4 Outside <br />126 <br />0 <br />SEI <br />218 <br />> 50% <br />BRK <br />5 Outside <br />122 <br />0 <br />SEI <br />AVG: <br />132 <br />STD. DEV. <br />8 <br />1Inside <br />118 <br />0 <br />SEI <br />2lnside <br />120 <br />0 <br />SE1 <br />3lnside <br />132 <br />0 <br />SE1 <br />4lnside <br />124 <br />0 <br />SE1 <br />5lnside <br />126 <br />0 <br />SE1 <br />AVG. <br />206 <br />AVG: <br />124 <br />STD. DEV. <br />8 <br />STD. DEV. <br />5 <br />DS -S14 49950 <br />202 <br />> 50% BRK 1 Outside <br />114 <br />0 <br />SE1 <br />S38139 <br />206 <br />> 50% BRK 2 Outside <br />138 <br />0 <br />SE1 <br />209 <br />> 50% BRK 3 Outside <br />126 <br />0 <br />SE1 <br />208 <br />> 50% BRK 4 Outside <br />110 <br />0 <br />SE1 <br />215 <br />> 50% BRK 5 Outside <br />1 132 <br />0 <br />SE1 <br />AVG: <br />124 <br />STD. DEV. <br />12 <br />1Inside <br />126 <br />0 <br />SE1 <br />2lnside <br />134 <br />0 <br />SE1 <br />3lnside <br />146 <br />0 <br />SE1 <br />4lnside <br />126 <br />0 <br />SE1 <br />5lnside <br />138 <br />0 <br />SE1 <br />AVG: <br />208 <br />AVG: <br />134 <br />STD. DEV. <br />5 <br />STD. DEV. <br />8 <br />BREAK DESCRIPTION (ASTM D6392 FU EXTRUSION: <br />AD1 <br />ADHESION FAILURE. SPECIMENS DELAMINATED UNDER THE BEAD. <br />AD <br />ADHESION FAILURE. <br />AD2 <br />ADHESION FAILURE. <br />BRK <br />BREAK IN SHEETING. <br />AD-WLD <br />BREAK THROUGH THE FILLET. <br />SE1 <br />BREAK AT OUTER EDGE OF SEAM. <br />SE1 <br />BREAK AT BOTTOM EDGE OF SEAM. <br />SE2 <br />BREAK AT INNER EDGE OF SEAM. <br />SE2 <br />BREAK AT TOP EDGE OF SEAM. <br />AD-BRK <br />BREAK IN FIRST SEAM AFTER SOME ADHESION FAILURE. <br />SE3 <br />BREAK AT BOTTOM EDGE OF SEAM (for PEEL only) <br />SIP <br />SEPARATION IN THE PLANE OF THE SHEET. <br />BRK1 <br />BREAK IN BOTTOM SHEETING. <br />BRK2 <br />BREAK IN TOP SHEETING. <br />AD-BRK <br />BREAK IN FIRST SEAM AFTER SOME ADHESION FAILURE. <br />HT <br />BREAK AT EDGE OF HOT TACK <br />SIP SEPARATION IN THE PLANE OF THE SHEET. <br />Precision Geosynthetic Laboratories k— <br />