Laserfiche WebLink
CLIENT: VECTOR ENGINEERING <br />PROJECT. Forward Landfill <br />DATE RECD: 22 -Aug -08 <br />MATERIAL: HDPE SEAM <br />SEAM TYPE: Weld <br />PGL JOB #: G081072 <br />QC'd By: 41 <br />TEST METHOD: ASTM D6392 <br />DATE REPORT: 22 -Aug -08 <br />Crosshead Speed: 2 in/min Crosshead Speed: 2 in/min <br />SHEAR EVALUATION PEEL EVALUATION <br />MAXIMUM % Locus PROJECT MAXIMUM % LOCUS PROJECT <br />SAMPLE PGL STRENGTH Elongation of SPEC. SPECIMEN STRENGTH INCURSION OF SPEC. <br />ID CONTROL # Ib�n width Break Ibrn width NUMBER Ibhn width % BREAK Iblin width <br />DS-D21B <br />50108 <br />190 <br />> 50% <br />BRK <br />1 Outside <br />159 <br />0 <br />SE3 <br />AD-BRK <br />OLDID73 <br />SE3 <br />191 <br />> 50% <br />BRK <br />2 Outside <br />165 <br />0 <br />SE3 <br />AD-BRK <br />200 <br />> 50% <br />BRK <br />3 Outside <br />159 <br />0 <br />SE3 <br />Extrusion <br />193 <br />> 50% <br />BRK <br />4 Outside <br />131 <br />0 <br />SE3 <br />200 <br />> 50% <br />BRK <br />5 Outside <br />135 <br />0 <br />SE3 <br />150 <br />AVG: <br />STD. DEV. <br />16 <br />60 <br />1Inside <br />N/A <br />2 Inside <br />3 Inside <br />4 Inside <br />5 Inside <br />AVG. <br />195 <br />90 AVG: <br />STD. DEV. <br />5 <br />STD. DEV. <br />DS -D29 <br />60109 <br />200 <br />> 50% <br />BRK <br />1 Outside <br />139 <br />0 <br />SE1 <br />D68/91 <br />191 <br />> 50% <br />BRK <br />2 Outside <br />149 <br />0 <br />SE1 <br />195 <br />> 50% <br />BRK <br />3 Outside <br />153 <br />0 <br />SE1 <br />Fusion <br />194 <br />> 50% <br />BRK <br />4 Outside <br />152 <br />0 <br />SEI <br />189 <br />> 50% <br />BRK <br />5 Outside <br />145 <br />0 <br />SE1 <br />148 <br />70 <br />AVG: <br />STD. DEV. <br />6 <br />142 <br />0 <br />SE1 <br />1Inside <br />2Inside <br />146 <br />0 <br />SE1 <br />3Inside <br />145 <br />0 <br />SEI <br />4Inside <br />165 <br />0 <br />SEI <br />5Inside <br />157 <br />0 <br />SE1 <br />AVG: <br />193 <br />90 AVG: <br />151 <br />70 <br />STD. DEV. <br />4 <br />STD. DEV. <br />10 <br />BREAK DESCRIPTION (ASTM D6392 FUSION): EXTRUSION: <br />A01 <br />AD <br />ADHESION FAILURE. <br />AD2 <br />BRK <br />BREAK IN SHEETING. <br />AD-WLD <br />SEI <br />BREAK AT OUTER EDGE OF SEAM. <br />SE1 <br />SE2 <br />BREAK AT INNER EDGE OF SEAM. <br />SE2 <br />AD-BRK <br />BREAK IN FIRST SEAM AFTER SOME ADHESION FAILURE. <br />SE3 <br />SIP <br />SEPARATION IN THE PLANE OF THE SHEET. <br />BRK1 <br />BRK2 <br />AD-BRK <br />HT <br />ADHESION FAILURE. SPECIMENS DELAMINATED UNDER THE BEAD. <br />ADHESION FAILURE. <br />BREAK THROUGH THE FILLET. <br />BREAK AT BOTTOM EDGE OF SEAM. <br />BREAK AT TOP EDGE OF SEAM. <br />BREAK AT BOTTOM EDGE OF SEAM (for PEEL only) <br />BREAK IN BOTTOM SHEETING. <br />BREAK IN TOP SHEETING. <br />BREAK IN FIRST SEAM AFTER SOME ADHESION FAILURE. <br />BREAK AT EDGE OF HOT TACK <br />450?" --ow <br />SIP SEPARATION IN THE PLANE OF THE SHEET.Gila <br />-- <br />YO <br />Precision Geosy nthetic Laboratories * +=a- <br />