Laserfiche WebLink
CLIENT. VECTOR ENGINEERING <br />PROJECT: Forward Landfill <br />DATE RECD: 22 -Aug -08 <br />TA 3. <br />SEAM PEEL AND SHEAR TEST RESULTS <br />MATERIAL: HDPE SEAM <br />SEAM TYPE: Fusion Weld <br />PGL JOB #: G081072 <br />QC'd By:41 <br />TEST METHOD: ASTM D6392 <br />DATE REPORT: 22 -Aug -08 <br />Crosshead Speed: 2 in/min Crosshead Speed. 2 in/min <br />SHEAR EVALUATION PEEL EVALUATION <br />MAXIMUM % Locus PROJECT MAXIMUM % LOCUS PROJECT <br />SAMPLE PGL STRENGTH Elongation of SPEC. SPECIMEN STRENGTH INCURSION OF SPEC. <br />ID CONTROL # IbCn width Break IbAn width NUMBER bfin width2 BREAKIbin width <br />DS -D32 <br />50112 <br />178 <br />> 50% <br />BRK 1 Outside <br />146 <br />0 <br />SE1 <br />SE2 <br />D94195 <br />BREAK IN FIRST SEAM AFTER SOME ADHESION FAILURE, <br />177 <br />> 50% <br />BRK 2 Outside <br />139 <br />0 <br />SE1 <br />BRK2 <br />182 <br />> 50% <br />BRK 3 Outside <br />154 <br />0 <br />SE1 <br />182 <br />> 50% <br />BRK 4 Outside <br />129 <br />0 <br />SE1 <br />190 <br />> 50% <br />BRK 5 Outside <br />126 <br />0 <br />SE1 <br />AVG: <br />139 <br />70 <br />STD. DEV. <br />12 <br />1Inside <br />124 <br />0 <br />SE1 <br />2lnside <br />145 <br />0 <br />SEI <br />3lnside <br />142 <br />0 <br />SE1 <br />4lnside <br />128 <br />0 <br />SE1 <br />5lnside <br />131 <br />0 <br />SE1 <br />AVG. <br />182 <br />AVG: <br />134 <br />70 <br />STD. DEV. <br />5 <br />STD. DEV. <br />9 <br />DS -D33 <br />50113 <br />184 <br />> 50% <br />BRK <br />1 Outside <br />116 <br />0 <br />SEI <br />D96197 <br />185 <br />> 50% <br />BRK <br />2 Outside <br />117 <br />0 <br />SE1 <br />190 <br />> 50% <br />BRK <br />3 Outside <br />123 <br />0 <br />SE1 <br />189 <br />> 50% <br />BRK <br />4 Outside <br />119 <br />0 <br />SEI <br />195 <br />> 50% <br />BRK <br />5 Outside <br />115 <br />0 <br />SE1 <br />118 <br />70 <br />AVG: <br />STD. DEV. <br />3 <br />144 <br />0 <br />SE1 <br />1Inside <br />2lnside <br />129 <br />0 <br />SE1 <br />3lnside <br />132 <br />0 <br />SE1 <br />4lnside <br />130 <br />0 <br />SE1 <br />5lnside <br />129 <br />0 <br />SEI <br />AVG: <br />188 <br />AVG: <br />133 <br />70 <br />STD. DEV. <br />4 <br />STD. DEV. <br />6 <br />BREAK DESCRIPTION (ASTIR D6392 FUSKft EXTRUSION: <br />ADI <br />AD <br />ADHESION FAILURE. <br />AD2 <br />BRK <br />BREAK IN SHEETING. <br />AD-WLD <br />SEI <br />BREAK AT OUTER EDGE OF SEAM. <br />SE1 <br />SE2 <br />BREAK AT INNER EDGE OF SEAM. <br />SE2 <br />AD-BRK <br />BREAK IN FIRST SEAM AFTER SOME ADHESION FAILURE, <br />SE3 <br />SIP <br />SEPARATION IN THE PLANE OF THE SHEET. <br />BRK1 <br />BRK2 <br />AD-BRK <br />HT <br />ADHESION FAILURE. SPECIMENS DELAMINATED UNDER THE BEAD, <br />ADHESION FAILURE. <br />BREAK THROUGH THE FILLET. <br />BREAK AT BOTTOM EDGE OF SEAM. <br />BREAK AT TOP EDGE OF SEAM. <br />BREAK AT BOTTOM EDGE OF SEAM (for PEEL only) <br />BREAK IN BOTTOM SHEETING. <br />BREAK IN TOP SHEETING. <br />BREAK IN FIRST SEAM AFTER SOME ADHESION FAILURE. <br />BREAK AT EDGE OF HOT TACK <br />SIP btYAKA I IUN IN I tit MANt Ur 1 tit Stitt 1. r y <br />MIMI <br />Precision eosynthetic Laboratories� .A <br />