Laserfiche WebLink
r <br />U <br />CLIENT., VECTOR ENGINEERING <br />PROJECT: Forward Landfill <br />DATE RECD: 22 -Aug -08 <br />TAM 6. <br />SEAM PEEL ARID SHEAR TEST RESULTS <br />MATERIAL: HDPE SEAM <br />SEAM TYPE: Fusion Weld <br />PGL JOB #. G081072 <br />QC'd By: 4! <br />TEST METHOD: ASTM D6392 <br />DATE REPORT: 22 -Aug -08 <br />Crosshead Speed: 2 in/min <br />Crosshead Speed: 2 in/min <br />AD <br />ADHESION FAILURE. <br />SHEAR EVALUATION <br />PEEL EVALUATION <br />BREAK IN SHEETING. <br />MAXIMUM <br />% <br />Locus <br />PROJECT <br />SE2 <br />MAXIMUM <br />% <br />LOCUS <br />PROJECT <br />SE3 <br />SIP <br />SAMPLE <br />PGL <br />STRENGTH <br />Elongation <br />of <br />SPEC. <br />SPECIMEN <br />STRENGTH <br />INCURSION <br />OF <br />SPEC. <br />ID <br />CONTROL # <br />Ib/in width <br />Break <br />Ibin width <br />NUMBER <br />Ib in width <br />% <br />BREAK <br />-n width <br />DS -D38 <br />50118 <br />188 <br />> 50% <br />BRK <br />1 Outside <br />150 <br />0 <br />SE1 <br />D101/102 <br />178 <br />> 50% <br />BRK <br />2 Outside <br />148 <br />0 <br />SEI <br />176 <br />> 50% <br />BRK <br />3 Outside <br />150 <br />0 <br />SE1 <br />182 <br />> 50% <br />BRK <br />4 Outside <br />155 <br />0 <br />SE1 <br />183 <br />> 50% <br />BRK <br />5 Outside <br />156 <br />0 <br />SE1 <br />AVG: <br />152 <br />70 <br />STD. DEV. <br />4 <br />1Inside <br />157 <br />0 <br />SE1 <br />2lnside <br />160 <br />0 <br />SE1 <br />3lnside <br />155 <br />0 <br />SE1 <br />4lnside <br />150 <br />0 <br />SE1 <br />5lnside <br />162 <br />0 <br />SE1 <br />AVG. <br />181 <br />90 <br />AVG: <br />157 <br />70 <br />STD. DEV. <br />5 <br />STD. DEV. <br />5 <br />DS -D39 <br />50119 <br />176 <br />> 50% <br />BRK <br />1 Outside <br />137 <br />0 <br />SE1 <br />D901103 <br />177 <br />> 50% <br />BRK <br />2 Outside <br />133 <br />0 <br />SEI <br />182 <br />> 50% <br />BRK <br />3 Outside <br />134 <br />0 <br />SE1 <br />181 <br />> 50% <br />BRK <br />4 Outside <br />129 <br />0 <br />SE1 <br />185 <br />> 50% <br />BRK <br />5 Outside <br />129 <br />0 <br />SE1 <br />AVG: <br />133 <br />70 <br />STD. DEV. <br />3 <br />1Inside <br />151 <br />0 <br />SE1 <br />2lnside <br />145 <br />0 <br />SE1 <br />3lnside <br />152 <br />0 <br />SE1 <br />4lnside <br />154 <br />0 <br />SE1 <br />5lnside <br />144 <br />1 0 <br />1 SE1 <br />AVG: <br />180 <br />90 <br />AVG: <br />149 <br />70 <br />STD. DEV. <br />4 <br />STD. DEV. <br />4 <br />BREAK DESCRIPTION (ASTM D6392 FUSION): EXTRUSION: <br />ADI <br />AD <br />ADHESION FAILURE. <br />AD2 <br />BRK <br />BREAK IN SHEETING. <br />AD-WLD <br />SE1 <br />BREAK AT OUTER EDGE OF SEAM. <br />SEI <br />SE2 <br />BREAK AT INNER EDGE OF SEAM. <br />SE2 <br />AD-BRK <br />BREAK IN FIRST SEAM AFTER SOME ADHESION FAILURE. <br />SE3 <br />SIP <br />SEPARATION IN THE PLANE OF THE SHEET. <br />BRK1 <br />BRK2 <br />AD-BRK <br />HT <br />ADHESION FAILURE. SPECIMENS DELAMINATED UNDER THE BEAD. <br />ADHESION FAILURE. <br />BREAK THROUGH THE FILLET. <br />BREAK AT BOTTOM EDGE OF SEAM. <br />BREAK AT TOP EDGE OF SEAM, <br />BREAK AT BOTTOM EDGE OF SEAM (for PEEL only) <br />BREAK IN BOTTOM SHEETING. <br />BREAK IN TOP SHEETING. <br />BREAK IN FIRST SEAM AFTER SOME ADHESION FAILURE, <br />BREAK AT EDGE OF HOT TACK <br />SIP __ <br />StF'AKA I IUN IN I Ht PLANt UI -I HE SHtt 1. _ I4p4p <br />...-_ *. <br />11 Ah A..1 <br />Precision Geosynthetic Laboratories -'j " <br />