Laserfiche WebLink
n <br />CLIENT. VECTOR ENGINEERING <br />PROJECT: Forward Landfill <br />DATE RECD: 18 -Aug -08 <br />r <br />MATERIAL: HDPE SEAM <br />SEAM TYPE: Fusion Weld <br />PGL JOB #. G081025 <br />QC'd By: <br />TEST METHOD: ASTM D6392 <br />DATE REPORT: 18 -Aug -08 <br />Crosshead Speed: 2 in/min Crosshead Speed: 2 in/min <br />SHEAR EVALUA '10N PEEL EVALUATION <br />MAXIMUM % Locus PROJECT MAXIMUM % LOCUS PROJECT <br />SAMPLE PGL STRENGTH Elongation of SPEC. SPECIMEN STRENGTH INCURSION OF SPEC. <br />ID CONTROL # Qhn width2 Break Ib/in width NUMBER &4n width) (%I BREAK lbfwidth <br />Ln <br />DS -S9 <br />49811 <br />209 <br />> 50% <br />BRK <br />1 Outside <br />116 <br />0 <br />SEI <br />AD-BRK <br />26/27 <br />SE3 <br />207 <br />> 50% <br />BRK <br />2 Outside <br />116 <br />0 <br />SE1 <br />AD-BRK <br />213 <br />> 50% <br />BRK <br />3 Outside <br />118 <br />0 <br />SE1 <br />210 <br />> 50% <br />BRK <br />4 Outside <br />110 <br />0 <br />SE1 <br />211 <br />> 50% <br />BRK <br />5 Outside <br />110 <br />0 <br />SE1 <br />114 <br />AVG: <br />STD. DEV. <br />4 <br />1Inside <br />112 <br />0 <br />SE1 <br />2lnside <br />128 <br />0 <br />SEI <br />3lnside <br />126 <br />0 <br />SE1 <br />4lnside <br />122 <br />0 <br />SEI <br />5Inside <br />118 <br />0 <br />SEI <br />AVG. <br />210 <br />AVG: <br />121 <br />STD. DEV. <br />2 <br />STD. DEV. <br />6 <br />DS -S10 49812 <br />204 <br />> 50% BRK 1 Outside <br />102 <br />0 <br />SE1 <br />27/28 <br />208 <br />> 50% BRK 2 Outside <br />106 <br />0 <br />SE1 <br />200 <br />> 50% BRK 3 Outside <br />106 <br />0 <br />SE1 <br />202 <br />> 50% BRK 4 Outside <br />102 <br />0 <br />SE1 <br />207 <br />> 50% BRK 5 Outside <br />102 <br />0 <br />SE1 <br />AVG: <br />104 <br />STD. DEV. <br />2 <br />1Inside <br />114 <br />0 <br />SE1 <br />2lnside <br />110 <br />0 <br />SE1 <br />3lnside <br />110 <br />0 <br />SEI <br />4lnside <br />112 <br />0 <br />SE1 <br />5 Onside <br />110 <br />0 <br />SE1 <br />AVG: <br />204 <br />AVG: <br />111 <br />STD. DEV. <br />3 <br />STD. DEV. <br />2 <br />BREAK DESCRIPTION (ASTNI D6392 FU EXTRUSION: <br />AD1 <br />AD <br />ADHESION FAILURE. <br />AD2 <br />BRK <br />BREAK IN SHEETING. <br />AD-WLD <br />SE1 <br />BREAK AT OUTER EDGE OF SEAM. <br />SE1 <br />SE2 <br />BREAK AT INNER EDGE OF SEAM. <br />SE2 <br />AD-BRK <br />BREAK IN FIRST SEAM AFTER SOME ADHESION FAILURE. <br />SE3 <br />SIP <br />SEPARATION IN THE PLANE OF THE SHEET. <br />BRK1 <br />BRK2 <br />AD-BRK <br />HT <br />ADHESION FAILURE. SPECIMENS DELAMINATED UNDER THE BEAD. <br />ADHESION FAILURE. <br />BREAK THROUGH THE FILLET. <br />BREAK AT BOTTOM EDGE OF SEAM. <br />BREAK AT TOP EDGE OF SEAM. <br />BREAK AT BOTTOM EDGE OF SEAM (for PEEL only) <br />BREAK IN BOTTOM SHEETING. <br />BREAK IN TOP SHEETING. <br />BREAK IN FIRST SEAM AFTER SOME ADHESION FAILURE. <br />BREAK AT EDGE OF HOT TACK <br />SIP strAKA I IUN IN 1 Ht rLANt Ur I Ht sett 1. <br />Precision Geosynthetic Laboratories <br />