Laserfiche WebLink
J <br />CLIENT: VECTOR ENGINEERING MATERIAL: HDPE SEAM <br />PROJECT. Forward Landfill SEAM TYPE: Fusion Weld <br />DATE RECD: 18-A1/g-08 PGL JOB #: G081025 <br />QC'd By.. <br />TEST METHOD: ASTM D6392 <br />DATE REPORT. • 18 -Aug -08 <br />Crosshead Speed: 2 in/min Crosshead Speed: 2 in/min <br />SHEAR EVALU ION PEEL EVALUATION <br />MAXIMUM % Locus PROJECT MAXIMUM % LOCUS PROJECT <br />SAMPLE PGL STRENGTH Elongation of SPEC. SPECIMEN STRENGTH INCURSION OF SPEC. <br />ID CONTROL # Iblin width Break Iblin width NUMBER /bAn widthl 12/212 BREAK IbAn width <br />DS -S7 <br />49809 <br />212 <br />> 50% <br />BRK <br />1 Outside <br />102 <br />0 <br />SEI <br />SE1 <br />1124 <br />SE2 <br />212 <br />> 50% <br />BRK <br />2 Outside <br />106 <br />0 <br />SE1 <br />SIP <br />SEPARATION IN THE PLANE OF THE SHEET. <br />BRKI <br />224 <br />> 50% <br />BRK <br />3 Outside <br />124 <br />0 <br />SEI <br />AD-BRK <br />BREAK IN FIRST SEAM AFTER SOME ADHESION FAILURE. <br />215 <br />> 50% <br />BRK <br />4 Outside <br />100 <br />0 <br />SEI <br />221 <br />> 50% <br />BRK <br />5 Outside <br />96 <br />0 <br />SEI <br />AVG: <br />106 <br />STD. DEV. <br />11 <br />1Inside <br />130 <br />0 <br />SEI <br />2lnside <br />124 <br />0 <br />SE1 <br />3lnside <br />124 <br />0 <br />SE1 <br />4lnside <br />120 <br />0 <br />SE1 <br />5lnside <br />124 <br />0 <br />SE1 <br />AVG. <br />217 <br />AVG: <br />124 <br />STD. DEV. <br />6 <br />STD. DEV. <br />4 <br />DS -S8 49810 <br />208 <br />> 50% BRK 1 Outside <br />124 <br />0 <br />SEI <br />24125 <br />205 <br />> 50% BRK 2 Outside <br />120 <br />0 <br />SE1 <br />217 <br />> 50% BRK 3 Outside <br />120 <br />0 <br />SE1 <br />211 <br />> 50% BRK 4 Outside <br />114 <br />0 <br />SE1 <br />207 <br />> 50% BRK 5 Outside <br />1 106 <br />0 <br />SE1 <br />AVG: <br />117 <br />STD. DEV. <br />7 <br />1Inside <br />116 <br />0 <br />SEI <br />2lnside <br />112 <br />0 <br />SE1 <br />3lnside <br />112 <br />0 <br />SE1 <br />4lnside <br />110 <br />0 <br />SE1 <br />5lnside <br />106 <br />0 <br />SE1 <br />AVG: <br />210 <br />AVG: <br />111 <br />STD. DEV. <br />5 <br />STD. DEV. <br />4 <br />BREAK BESGRIPTION (ASTM 06392 FUSION): EXTRUSION: <br />ADI <br />ADHESION FAILURE. SPECIMENS DELAMINATED UNDER THE BEAD. <br />AD <br />ADHESION FAILURE. <br />AD2 <br />ADHESION FAILURE. <br />BRK <br />BREAK IN SHEETING. <br />AD-WLD <br />BREAK THROUGH THE FILLET. <br />SEI <br />BREAK AT OUTER EDGE OF SEAM. <br />SE1 <br />BREAK AT BOTTOM EDGE OF SEAM. <br />SE2 <br />BREAK AT INNER EDGE OF SEAM. <br />SE2 <br />BREAK AT TOP EDGE OF SEAM. <br />AD-BRK <br />BREAK IN FIRST SEAM AFTER SOME ADHESION FAILURE. <br />SE3 <br />BREAK AT BOTTOM EDGE OF SEAM (for PEEL only) <br />SIP <br />SEPARATION IN THE PLANE OF THE SHEET. <br />BRKI <br />BREAK IN BOTTOM SHEETING. <br />BRK2 <br />BREAK IN TOP SHEETING. <br />AD-BRK <br />BREAK IN FIRST SEAM AFTER SOME ADHESION FAILURE. <br />HT <br />BREAK AT EDGE OF HOT TACK <br />SIP SEPARATION IN THE PLANE OF THE SHEET. ° .. <br />I <br />OKI <br />Precision Geosynthetic Laboratories <br />