Laserfiche WebLink
r� <br />u <br />CLIENT. VECTOR ENGINEERING <br />PROJECT Forward Landfill <br />DATE REC D: 22 -Aug -08 <br />Tin 10. <br />SEAM PEEL AND SHEAR TEST RESULTS <br />MATERIAL: HDPE SEAM <br />SEAM TYPE: Fusion Weld <br />PGL JOB #. G081072 <br />QC'd By. <br />TEST METHOD: ASTM D6392 <br />DATE REPORT: 22 -Aug -08 <br />Crosshead Speed: 2 in/min <br />Crosshead Speed: 2 in/min <br />SHEAR EVALUATION <br />PEEL EVALUATION <br />AD2 <br />MAXIMUM <br />% <br />LOCUS <br />PROJECT <br />MAXIMUM % Locus PROJECT <br />SAMPLE PGL STRENGTH Elongation of SPEC. <br />SPECIMEN <br />STRENGTH <br />INCURSION <br />OF <br />SPEC. <br />ID CONTROL #IbLin width Break Ibfin width <br />NUMBER <br />lin width <br />% <br />BREAK <br />Iblin width <br />DS -D46 <br />50126 <br />181 <br />> 50% <br />BRK <br />1 Outside <br />128 <br />0 <br />SE1 <br />D1161117 <br />179 <br />> 50% <br />BRK <br />2 Outside <br />124 <br />0 <br />SE1 <br />183 <br />> 50% <br />BRK <br />3 Outside <br />142 <br />0 <br />SE1 <br />180 <br />> 50% <br />BRK <br />4 Outside <br />120 <br />0 <br />SE1 <br />186 <br />> 50% <br />BRK <br />5 Outside <br />134 <br />0 <br />SE1 <br />AVG: <br />130 <br />70 <br />STD. DEV. <br />9 <br />1Inside <br />126 <br />0 <br />SE1 <br />2lnside <br />126 <br />0 <br />SE1 <br />3lnside <br />128 <br />0 <br />SE1 <br />4lnside <br />138 <br />0 <br />SE1 <br />5lnside <br />129 <br />0 <br />SE1 <br />AVG. <br />182 <br />90 <br />AVG: <br />129 <br />70 <br />STD. DEV. <br />3 <br />STD. DEV. <br />5 <br />DS -D47 <br />50127 <br />176 <br />>50% <br />BRK <br />1 Outside <br />124 <br />0 <br />SE1 <br />D118/119 <br />177 <br />> 50% <br />BRK <br />2 Outside <br />126 <br />0 <br />SE1 <br />181 <br />> 50% <br />BRK <br />3 Outside <br />138 <br />0 <br />SE1 <br />180 <br />> 50% <br />BRK <br />4 Outside <br />120 <br />0 <br />SE1 <br />186 <br />> 50% <br />BRK <br />5 Outside <br />132 <br />0 <br />SE1 <br />AVG: <br />128 <br />70 <br />STD. DEV. <br />7 <br />1Inside <br />124 <br />0 <br />SE1 <br />2lnside <br />126 <br />0 <br />SE1 <br />3lnside <br />138 <br />0 <br />SE1 <br />4lnside <br />120 <br />0 <br />SE1 <br />5lnside <br />132 <br />0 <br />SE1 <br />AVG: <br />180 <br />90 <br />AVG: <br />128 <br />70 <br />STD. DEV. <br />4 <br />STD. DEV. <br />7 <br />BREAK DESCRIPTION (ASTNI D6392 FU EXTRUSION: <br />AD1 <br />AD <br />ADHESION FAILURE. <br />AD2 <br />BRK <br />BREAK IN SHEETING. <br />AD-WLD <br />SEI <br />BREAK AT OUTER EDGE OF SEAM. <br />SE1 <br />SE2 <br />BREAK AT INNER EDGE OF SEAM. <br />SE2 <br />AD-BRK <br />BREAK IN FIRST SEAM AFTER SOME ADHESION FAILURE. <br />SE3 <br />SIP <br />SEPARATION IN THE PLANE OF THE SHEET. <br />BRKI <br />BRK2 <br />AD-BRK <br />HT <br />ADHESION FAILURE. SPECIMENS DELAMINATED UNDER THE BEAD. <br />ADHESION FAILURE. <br />BREAK THROUGH THE FILLET. <br />BREAK AT BOTTOM EDGE OF SEAM. <br />BREAK AT TOP EDGE OF SEAM. <br />BREAK AT BOTTOM EDGE OF SEAM (for PEEL only) <br />BREAK IN BOTTOM SHEETING. <br />BREAK IN TOP SHEETING. <br />BREAK IN FIRST SEAM AFTER SOME ADHESION FAILURE. <br />BREAK AT EDGE OF HOT TACK <br />SIP StI'AKA I IUN IN I ht NLANL OF I HE Stitt 1. <br />Precision Geosynthetic Laboratories ,�,.. <br />