Laserfiche WebLink
r� <br />U <br />CLIENT: VECTOR ENGINEERING <br />PROJECT: Forward Landfill <br />DATE RECD: 22 -Aug -08 <br />T* 11. <br />lv_ 01 <br />MATERIAL: HDPE SEAM <br />SEAM TYPE: Fusion Weld <br />PGL JOB #: G081072 <br />QC'd By. <br />TEST METHOD: ASTM D6392 <br />DATE REPORT: 22 -Aug -08 <br />Crosshead Speed: 2 in/min Crosshead Speed: 2 in/min <br />SHEAR EVALUATION PEEL EVALUATION <br />MAXIMUM % Locus PROJECT MAXIMUM % LOCUS PROJECT <br />SAMPLE PGL STRENGTH Elongation of SPEC. SPECIMEN STRENGTH INCURSION OF SPEC. <br />ID CONTROL # Ib/in width2 Break Iblin width NUMBER &fin width % BREAK li*n width <br />DS -D48 <br />50128 <br />180 <br />> 50% <br />BRK <br />1 Outside <br />138 <br />0 <br />SE1 <br />AD-BRK <br />D1191120 <br />SE3 <br />182 <br />> 50% <br />BRK <br />2 Outside <br />140 <br />0 <br />SE1 <br />AD-BRK <br />180 <br />> 50% <br />BRK <br />3 Outside <br />142 <br />0 <br />SE1 <br />177 <br />> 50% <br />BRK <br />4 Outside <br />130 <br />0 <br />SE1 <br />186 <br />> 50% <br />BRK <br />5 Outside <br />125 <br />0 <br />SE1 <br />AVG: <br />135 <br />70 <br />STD. DEV. <br />7 <br />1Inside <br />131 <br />0 <br />SE1 <br />2lnside <br />128 <br />0 <br />SE1 <br />3lnside <br />130 <br />0 <br />SE1 <br />4lnside <br />132 <br />0 <br />SE1 <br />5lnside <br />140 <br />0 <br />SE1 <br />AVG. <br />181 <br />90 AVG: <br />132 <br />70 <br />STD. DEV. <br />3 <br />STD. DEV. <br />5 <br />DS -D49 <br />50129 <br />184 <br />> 50% <br />BRK <br />1 Outside <br />136 <br />0 <br />SE1 <br />D113/121 <br />184 <br />>50% <br />BRK <br />2 Outside <br />127 <br />0 <br />SE1 <br />189 <br />> 50% <br />BRK <br />3 Outside <br />151 <br />0 <br />SE1 <br />188 <br />>50% <br />BRK <br />4 Outside <br />119 <br />0 <br />SE1 <br />195 <br />> 50% <br />BRK <br />5 Outside <br />135 <br />0 <br />SE1 <br />AVG: <br />134 <br />70 <br />STD. DEV. <br />12 <br />1Inside <br />130 <br />0 <br />SE1 <br />2lnside <br />144 <br />0 <br />SE1 <br />3lnside <br />142 <br />0 <br />SE1 <br />4lnside <br />128 <br />0 <br />SE1 <br />5lnside <br />130 <br />1 0 <br />SE1 <br />AVG: <br />188 <br />90 AVG: <br />135 <br />70 <br />STD. DEV. <br />4 <br />1 STD. DEV. <br />8 <br />BREAK DESCRIPTION (ASTM D6392 FUSION): EXTRUSION: <br />ADI <br />AD <br />ADHESION FAILURE. <br />AD2 <br />BRK <br />BREAK IN SHEETING. <br />AD-WLD <br />SEI <br />BREAK AT OUTER EDGE OF SEAM. <br />SE1 <br />SE2 <br />BREAK AT INNER EDGE OF SEAM. <br />SE2 <br />AD-BRK <br />BREAK IN FIRST SEAM AFTER SOME ADHESION FAILURE. <br />SE3 <br />SIP <br />SEPARATION IN THE PLANE OF THE SHEET. <br />BRK1 <br />BRK2 <br />AD-BRK <br />HT <br />ADHESION FAILURE. SPECIMENS DELAMINATED UNDER THE BEAD. <br />ADHESION FAILURE. <br />BREAK THROUGH THE FILLET. <br />BREAK AT BOTTOM EDGE OF SEAM. <br />BREAK AT TOP EDGE OF SEAM. <br />BREAK AT BOTTOM EDGE OF SEAM (for PEEL only) <br />BREAK IN BOTTOM SHEETING, <br />BREAK IN TOP SHEETING. <br />BREAK IN FIRST SEAM AFTER SOME ADHESION FAILURE. <br />BREAK AT EDGE OF HOT TACK <br />SIP 5tF'AKA 1 IUN IN I HE NLANL Ur 1 HE SHtt 1. _-- <br />"221091" Precision Geosynthetic Laboratories - <br />