COVER
<br />SHER WIN
<br />WILLIAMS.
<br />Part A: 36 months, unopened
<br />Part B: 24 months, unopened
<br />Store indoors at 40°F (4.5°C) to
<br />100°F (38°C)
<br />102°F (39°C), TCC, mixed
<br />Reducer*: VOC Restricted Areas (<250 g/L):
<br />Reduction not recommended
<br />Clean Up: Reducer R6K30 or R7K225
<br />'Other areas (<340 g/L): Reducer R6K30 or R7K225 up to 5% by volume.
<br />Choose a reducer that is compliant in your area. Confirm compliance with state
<br />and local air quality rules before use.
<br />Shelf Life:
<br />Flash Point:
<br />Recommended Spreading Rate Per coat:
<br />Minimum Maximum
<br />Wet mils (microns) 3.0 (75) 4.5 (112)
<br />Dry mils (microns) 2.0 (50) 3.0 (75)
<br />—Coverage sq ft/gal (m2/L) 380 (9.3) 570 (14.0)
<br />Theoretical coverage sq ft/gal
<br />(m2 /L) @ 1 mil / 25 microns dft
<br />NOTE: Brush or roll application may require multiple coats to
<br />achieve maximum film thickness and uniformity of appearance.
<br />1136 (27.8)
<br />Drying Schedule @ 3.0 mils wet (75 microns):
<br />@ 50°F/10°C @ 77°F/25°C @ 100°F/38°C
<br />50% RH
<br />To touch: 16 hours 2 hours 30 minutes
<br />To handle: 24 hours 10 hours 2 hours
<br />foot traffic: 24 hours 12 hours 8 hours
<br />heavy traffic: 5 days 72 hours 48 hours
<br />To recoat:
<br />minimum: 24 hours 12 hours 2 hours
<br />maximum: 3 days 48 hours 24 hours
<br />To cure: 7 days 7 days 5 days
<br />If maximum recoat time is exceeded, abrade surface before recoating.
<br />Drying time is temperature, humidity, and film thickness dependent.
<br />Pot Life: 5 hours 4 hours 45 minutes
<br />Sweat-in-Time: None required
<br />ArmorSeal ARMORSEAL HS POLYURETHANE
<br />Heavy FLOOR ENAMEL
<br />Duty Floor
<br />Coatings
<br />PART A
<br />
<br />B65-220
<br />
<br />SERIES
<br />PART B
<br />
<br />B65V220
<br />
<br />HARDENER
<br />Revised: March 24, 2022
<br /> PRODUCT INFORMATION
<br />8.46
<br />PRODUCT DESCRIPTION
<br />ARMORSEAL HS POLYURETHANE FLOOR ENAMEL is a
<br />heavy duty, two component, exterior/interior, high solids, polyester-
<br />aliphatic urethane industrial floor coating. Provides a high gloss,
<br />excellent chemical resistance, color retention, and chalk resistance.
<br />Outstanding resistance a wide range of chemical, weather, and
<br />mechanical conditions
<br />Abrasion and impact resistant
<br />Superior exterior color and gloss retention
<br />Outstanding application properties
<br />PRODUCT CHARACTERISTICS
<br />Finish: Gloss
<br />Color: Wide range of colors available
<br />Volume Solids: 71% ± 2%, mixed, may vary by color
<br />Weight Solids: 90% ± 2%, mixed, may vary by color
<br />VOC (EPA Method 24): <250 g/L; 2.1 lb/gal, mixed
<br />Mix Ratio: 2:1 by volume
<br />RECOMMENDED USES
<br />For industrial, commercial, or marine floor use where a heavy
<br />duty polyurethane floor coating is required
<br />For use over prepared concrete and steel
<br />Resists splash, spillage, and fumes of dilute acids, alkalies,
<br />solvents, and fuels
<br />Exterior floors (helipads)
<br />Auto service centers, computer rooms
<br />Airport hangars (skydrol resistance)
<br />Suitable for use in USDA inspected facilities.
<br />PERFORMANCE CHARACTERISTICS
<br />Test Name Test Method Results
<br />Abrasion
<br />Resistance
<br />ASTM 04060,
<br />CS17 wheel, 1000
<br />cycles, 1 kg load
<br />63 mg loss
<br />(average of 5 trials)
<br />Adhesion, steel
<br />(epoxy primer)
<br />ASTM 03359
<br />Method B; ASTM
<br />04541
<br />5B, 100%
<br />Retention (ASTM
<br />D3359); 1200 psi
<br />(ASTM D4541)
<br />Adhesion,
<br />concrete
<br />(epoxy primer)
<br />ASTM D4541 350 psi, 100% concrete failure
<br />Direct Impact
<br />Resistance ASTM D2794 100 in. lb.
<br />Dry Heat
<br />Resistance ASTM D2485 200°F (93°C), 250°F
<br />(121°C) intermittent
<br />Exterior Durability 2 years at 45°
<br />South
<br />Excellent, 87% gloss
<br />retention
<br />Flexibility ASTM D522, 180°
<br />bend, 1/4" mandrel Passes
<br />Humidity
<br />Resistance
<br />ASTM D4585,
<br />100°F (38°C), 2000
<br />hours
<br />No blistering,
<br />cracking, softening or
<br />delamination
<br />Pencil Hardness ASTM 03363 H
<br />Salt Fog
<br />Resistance,
<br />with primer
<br />ASTM B117, 1000
<br />hours
<br />Rating 10 per ASTM
<br />D610 for rusting, less
<br />than 1/16" creepage
<br />at scribe. No
<br />blistering, cracking,
<br />softening, or
<br />delamination of the
<br />film.
<br />Slip Resistance,
<br />Floors
<br />ASTM C1028**, .60
<br />Minimum Static Co-
<br />efficient of Friction
<br />Passes wet and dry
<br />without SharkGrip
<br />Additive, and dry with
<br />SharkGrip
<br />Additive
<br />**Test method withdrawn in 2014 without replacement
<br />www.sherwin-williams.com/protective continued on back
|