COMPLIANCE INFO_1990-2001 - Laserfiche WebLink

Home Browse Search

0 • & 0 0 Dimensions and tolerances Pipe dimensions Workmanship The pipe and fittings shall be free from all defects including delaminations, Pipe shall be manufactured to steel pipe outside diameters for all sizes. Pipe indentations, pinholes, foreign inclusions, bubbles and resin -starved areas outside diameter tolerances shall not exceed ± 1 percent. which, due to their nature, degree or extent, detrimentally affect the strength Wall thickness 0 0 and serviceability of pipe or fittings. The pipe and fittings shall be as The total wall thickness of pipe furnished under this specification shall not at uniform as commercially practicable in color, opacity, density and other any point be greater than 120 percent nor less than 871/2 percent of the physical properties. nominal thickness. Fittings dimensions Testing Proof testing All fittings supplied under this specification shall have face-to-face dimensions Fittings shall be hydrostatically tested according to UL specifications by the and laying lengths as specified in the manufacturer's literature. manufacturer to rated pressure prior to shipment for signs of leakage or porosity. Physical and mechanical ASTM classification Quality control testing property requirements Pipe shall conform to ASTM D2310 standard classification RTRP-11CZ and A sample of pipe shall be tested at a frequency specified by UL to determine ASTM D2996 specification designation RTRP-11 CZ 5430. conformance of the materials to the short-term circumferential stress requirement tabulated above. Minimum ASTM Marking Each component shall be marked to show the following: Property Units Value* Method Underwriters' Laboratories listing mark Tensile strength Manufacturer's name Longitudinal 103 psi D2105 Maximum pressure rating 224.5 Circumferential 103 psi 65.0 D1599 MPa 448 Important notice This literature and the information and recommendations it contains are Tensile modulus based on data reasonably believed to be reliable. However, such factors as Longitudinal 106 psi variations in environment, application or installation, changes in operating 19.3 D2105 Circumferential 106 GPa psi 4.0 — procedures, or extrapolation of data may cause different results. Ameron GPa 27.6 makes no representation or warranty, express or implied, including warranties Compressive strength of merchantability or fitness for purpose, as to the accuracy, adequacy or Longitudinal 103 psi 32.5 D695 completeness of the recommendations or information contained herein. MPa 224 Ameron assumes no liability whatsoever in connection with this literature Compressive modulus or the information or recommendations it contains. Longitudinal 106 psi 2.8 D695 GPa 12.3 Written comments regarding this document are invited. Please write Long-term hydrostatic design basis 3 Static 10 psi 31.5 D2992(B) Engineering Manager, Ameron Fiberglass Pipe Division. MPa 217 Thermal expansion Linear 10-6in/in/°F 9.0* * D696 10-6mm/mm/0C 16.2* * Stiffness factor* * * D2412 (in) (mm) (lb • in3/in2) (N • m) 2 50 45 5.1 3 80 65 7.3 4 100 55 6.2 6 150 250 28 * Based on structural wall thickness. * * Maximum value. * * * At 5% diametric deflection and room temperature. Joining methods Tapered bell x spigot adhesive joints Pipe and fittings shall be joined by means of a matching tapered adhesive joint. Adhesive for joining components shall be compatible with all intended fluids. Adhesive system shall be used according to manufacturer's recommendations. Adapters and crossovers The following adapters and crossovers shall be provided as required: Threaded adapter: bell x male Threaded adapter: bellx female Threaded adapter: spigot x male Threaded adapter: spigot x female Flanges Flanges shall be two piece (Van Stone) type provided with raised grooves on • • the sealing face. Fiberglass reinforced stub ends are to be adhesive bonded to the pipe or fitting.